微加工:剝離

更新時間:2015-08-06      瀏覽次數(shù):3222

Lift-off process in microstructuring technology is a method of creating structures (patterning) of a target material on the surface of a substrate (ex. wafer) using a sacrificial material (ex. Photoresist). It is an additive technique as opposed to more traditional subtracting technique like etching. The scale of the structures can vary from the nanoscale up to the centimeter scale or further, but are typically of micrometric dimensions.

Process

An inverse pattern is first created in the sacrificial stencil layer (ex. photoresist), deposited on the surface of the substrate. This is done by etching openings through the layer so that the target material can reach the surface of the substrate in those regions, where the final pattern is to be created. The target material is deposited over the whole area of the wafer, reaching the surface of the substrate in the etched regions and staying on the top of the sacrificial layer in the regions, where it was not previously etched. When the sacrificial layer is washed away (photoresist in a solvent), the material on the top is lifted-off and washed together with the sacrificial layer below. After the lift-off, the target material remains only in the regions where it had a direct contact with the substrate.

·       Substrate is prepared

·       Sacrificial layer is deposited and an inverse pattern is created (ex. photoresist is exposed and developed. Depending on the resist various methods can be used, such as Extreme ultraviolet lithography - EUVL or Electron beam lithography - EBL. The photoresist is removed in the areas, where the target material is to be located, creating an inverse pattern.)

·       Target material (usually a thin metal layer) is deposited (on the whole surface of the wafer). This layer covers the remaining resist as well as parts of the wafer that were cleaned of the resist in the previous developing step.

·       The rest of the sacrificial material (ex. photoresist) is washed out together with parts of the target material covering it, only the material that was in the "holes" having direct contact with the underlying layer (substrate/wafer) stays

Advantages

Lift-off is applied in cases where a direct etching of structural material would have undesirable effects on the layer below.

Disadvantages

There are 3 major problems with lift-off:

Retention

This is the worst problem for liftoff processes. If this problem occurs, unwanted parts of the metal layer will remain on the wafer. This can be caused by different situations. The resist below the parts that should have been lifted off could not have dissolved properly. Also, it is possible that the metal has adhered so well to the parts that should remain that it prevents lift-off.

Ears

When the metal is deposited, and it covers the sidewalls of the resist, "ears" can be formed. These are made of the metal along the sidewall which will be standing upwards from the surface. Also, it is possible that these ears will fall over on the surface, causing an unwanted shape on the substrate.

If the ears remain on the surface, the risk remains that these ears will go through different layers put on top of the wafer and they might cause unwanted connections.

Redeposition

During the liftoff process it is possible that particles of metal will become reattached to the surface, at a random location. It is very difficult to remove these particles after the wafer has dried.

Use

Lift-off process is used mostly to create metallic interconnections.
There are several types of lift-off processes, and what can be achieved depends highly on the actual process being used. Very fine structures have been used using EBL, for instance. The lift-off process can also involve multiple layers of different types of resist. This can for instance be used to create shapes that will prevent side walls of the resist being covered in the metal deposition stage.

*Please contact us if there is problem using this passage* 

返回列表

版權(quán)所有©2025 那諾中國有限公司 All Rights Reserved   備案號:   sitemap.xml   技術(shù)支持:化工儀器網(wǎng)   管理登陸
国产在线无码av完整版在线观看| 色翁荡息肉欲500篇| www.天堂av| aj38水蜜桃| 91久久久久久久久久| 少妇久久久| 性色a∨亚洲一区二区三区老狼| 天堂…中文在线最新版在线| AV人摸人人人澡人人超碰小说| 免费无码不卡视频在线观看| 久久久精品人妻一区二区三区四 | 日韩a人毛片精品无人区乱码| 九九九精品成人免费视频7| 丹阳市| 聂拉木县| 互换人妻| 臭小子晚上让你爽个够视频| 丰满少妇高潮惨叫久久久久| 成人性生生活性生交一| 99成人在线| 日韩av在线直播| 奇米影视亚洲春色| 亚洲av少妇| 亚洲精品xxx| 男女xxx| 高潮毛片7777777毛片| 国产伦精品一区二区三区男技| 99热免费| 四虎影| 泊头市| 伊人久久成综合久久影院| 国产青榴视频在线观看| 中文乱码字幕高清一区二区| 欧美成a高清在线观看| 国产成人999黄网站在线观看| 精品久久久久久无码专区不卡| 久久精品国产久精国产思思| 热99re久久精品这里都是精品免费| 狠狠色噜噜狠狠狠狠97| 国产香蕉视频在线播放 | 伊人久久久大香线蕉综合直播|